The latest LED dental curing devices claim sufficient curing of restorative materials with short curing times. This study evaluates mechanical and chemical properties as a function of curing time of two commercial composite filling materials cured with three different LED lamps.
The composites were Filtek Z250 (3M ESPE) and Tetric EvoCeram (Ivoclar Vivadent) and the LED curing devices were bluephase 16i (Ivoclar Vivadent), L.E.Demetron II (Kerr) and Mini L.E.D. (Satelec). Control samples were cured with a QTH-lamp (VCL 400, Kerr). The wear resistance after simulated tooth brushing, degree of conversion, curing depth, and amounts of residual monomers were measured after different curing times.
The results of this study show that short curing time with high-intensity LEDs may influence the bulk properties of the materials, resulting in lower curing depth and increased residual monomer content. The measured surface properties of the materials, degree of conversion and wear resistance, were not affected by short curing times to the same extent. This study demonstrates that reduced exposure time with high intensity LEDs can result in composite restorations with inferior curing depth and increased leaching of monomers. Dentists are recommended to use sufficient curing times even with high intensity LEDs to ensure adequate curing and minimize the risk of monomer leaching.
Effekt av kort herdetid på kjemiske og mekaniske egenskaper til kompositter. Kopperud HBM, Johnsen GF, Lamolle SF, Kleven IJS, Wellendorf H, Haugen HJ.
Nor Tannlegeforen Tidende 2014; 124: 356-362.